EVA 1003 VN 4 TOTAI FRANCE
10
CompareTechnical Data Sheet
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Haze ratio | ISO 14782 | 2.5 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 | 0.4 g/10min | |
| density | ISO 1183 | 0.935 g/cm³ |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation at break | ISO 527-3 | 310 % | |
| Elmendorf tear strength | ISO 6383-2 | 28 N/mm | |
| ISO 6383-2 | 13 N/mm | ||
| Drop hammer test | ISO 7765-1 | 650 g | |
| Elastic modulus | ISO 527-2 | 70 Mpa | |
| Yield tensile strength | ISO 527-3 | 5 Mpa | |
| ISO 527-3 | 6.5 Mpa | ||
| Tensile strength at break | ISO 527-3 | 38 Mpa | |
| ISO 527-3 | 38 Mpa | ||
| elongation at break | ISO 527-3 | 590 % |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| VA content | Total Petrochemicals | 13.5 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melting temperature | ISO 11357 | 92 °C | |
| vicat | ISO 306 | 74 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.