PA6 ADDINYL B2 ZV20 ADDIPLAST FRANCE

Properties:

High rigidity good heat aging resistance high heat resistance

Typical Applications:

Parts under the hood of a car applications in the automotive industry

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Parts under the hood of a car \| applications in the automotive industry
Properties:	High rigidity \| good heat aging resistance \| high heat resistance

Certificates

No Data...

Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	简支梁Notched冲击强度	ISO 179/1eA	11.0	kJ/m²
	Impact strength of cantilever beam gap	简支梁Unnotched冲击强度	ISO 179/1eU	50	kJ/m²
		Impact strength of cantilever beam gap	悬壁梁Notched冲击强度	ISO 180/1A	16.0	kJ/m²
			Impact strength of cantilever beam gap	弹性模量	ISO 178	5600	MPa
				Impact strength of cantilever beam gap	弹性模量	ISO 178	3400	MPa
				Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	9.0	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	45	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	6.0	kJ/m²
Elongation at Break	有条件的，Yield，23°C	ISO 527-2	5.0	%
Elongation at Break	Elongation at Break	Yield，23°C	ISO 527-2	3.0	%
tensile strength	有条件的，Break，23°C	ISO 527-2	85.0	MPa
tensile strength	tensile strength	Break，23°C	ISO 527-2	145	MPa
Tensile stress (fracture)	，85.0	ISO 527-2	145	MPa
Tensile strain (fracture)	，5.0	ISO 527-2	3.0	%
Bending modulus	，3400	ISO 178	5600	MPa
Charpy Notched Impact Strength	，11	ISO 179/1eA	6.0	KJ/m2
Charpy Notched Impact Strength	Charpy Notched Impact Strength	，50	ISO 179/1eU	45	KJ/m2
Impact strength of cantilever beam gap	，16.0	ISO 180/1A	9.00	KJ/m2
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.80MPaAnnealed	ISO 75-2/Af	210	°C
	Hot deformation temperature	线膨胀系数	ASTME831	3.5E-05	cm/cm／°C
	Hot deformation temperature	Hot deformation temperature	Melting Temperature	ISO 3146/C2	220	°C
Linear coefficient of thermal expansion	，--	ASTM E831	0.000035	cm/cm/℃
Melting temperature	，-DSC法	ISO 3416	220	℃
Hot deformation temperature	1.8 MPa，Unannealed，-HDT	ISO 75-2/Af	210	℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density	，--	ISO 1183/A	1.29	g/cm3
density	density		ISO 1183	1.29	g/cm³
Shore hardness	，74	ISO 868	83
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	1E+15	Ω.cm
Dissipation factor	体积电阻	IEC 60093	1E+11	Ω.cm
Dissipation factor	Dissipation factor	相对漏电起痕指数	IEC 60112	550	V
Dielectric strength		IEC 60243-1	33.0	KV/mm
Dielectric strength	Dielectric strength	有条件的	IEC 60243-1	30.0	KV/mm
Volume resistivity	，1.0E+11	IEC 60093	1E+15	ohm-cm
Leakage Traceability Index (Solution A)	，--	IEC 60112	450	V
Dielectric strength	，30	IEC 60243-1	33	kv/mm
hardness	Test Condition	Test Method	Test Result	Test Unit
Hardness (Shore A)		ISO 868	83
Shore hardness	D型, 有条件	ISO 868	74

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.