PC/ABS CY6025-8B8D004 SABIC INNOVATIVE NANSHA

Form：Granules | Grade：Flame retardant grade

Properties:

High temperature resistanHigh mobility

Typical Applications:

Electrical applicationsHome appliance components

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical applications \| Home appliance components
Properties:	High temperature resistan \| High mobility

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	11	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.00mm	UL 94	V-1
	UL flame retardant rating	1.20mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	1.50mm	UL 94	5VB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
yield		Internal Method	59.0	Mpa
	yield		ASTM D638	56.0	Mpa
	yield	yield		ISO 527-2/50	57.0	Mpa
crack		Internal Method	79	%
	crack		ASTM D638	99	%
	crack	crack		ISO 527-2/50	99	%
50.0mm span		ASTM D790	2570	Mpa
--5		ISO 178	2880	Mpa
--6		ISO 178	96.0	Mpa
Yield, 50.0mm span		ASTM D790	89.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI		UL 746	60.0	°C
0.45MPa, unannealed, 64.0mm span		ISO 75-2/Bf	83.6	°C
1.8MPa, unannealed, 3.20mm		ASTM D648	72.0	°C
1.8MPa, unannealed, 64.0mm span of		ISO 75-2/Af	74.0	°C
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	7E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	6.7E-05	cm/cm/°C
RTI Elec		UL 746	60.0	°C
RTI Imp		UL 746	60.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Saturation,23°C	ISO 62	0.29	%
melt mass-flow rate	260°C/2.16kg	ASTM D1238	28	g/10min
Shrinkage rate	MD	Internal Method	0.23	%
Shrinkage rate	Shrinkage rate	TD	Internal Method	0.31	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		ASTM D257	1E+15	ohms
Compared to the anti leakage trace index	CTI	UL 746	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.