ABS EX120 UMG JAPAN

Form：Granules | Grade：Injection grade

Properties:

High mobilityFlame retardant

Typical Applications:

Bottle capHome appliance componentspartsAutomotive ApplicationsFitness equipment

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Bottle cap \| Home appliance components \| parts \| Automotive Applications \| Fitness equipment
Properties:	High mobility \| Flame retardant

Certificates

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			流动
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.0mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.5mm	UL 94	HB
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate			26	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus		ASTM D790/ISO 178	2.600	kg/cm²(MPa)[Lb/in²]
Charpy Notched Impact Strength		ASTM D256/ISO 179	16	kg·cm/cm(J/M)ft·lb/in
Charpy Notched Impact Strength	Charpy Notched Impact Strength			16	kJ/m²
Bending modulus			2500	Mpa
Tensile modulus	23°C	ISO 527-2	2300	Mpa
tensile strength	23°C	ISO 527-2	44.0	Mpa
Bending modulus	23°C	ISO 178	2500	Mpa
bending strength	23°C	ISO 178	71.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Combustibility (rate)		UL 94	HB
Hot deformation temperature	HDT	ASTM D648/ISO 75	79	℃（℉）
Hot deformation temperature	Hot deformation temperature	HDT		79	°C
UL flame retardant rating		UL 94	HB
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	79.0	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	8E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate		ASTM D1238/ISO 1133	26	g/10min
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	26.0	cm3/10min
Shrinkage rate	MD：23°C	ISO 294-4	0.40-0.60	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale,23°C	ISO 2039-2	106

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.