Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.20 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 11 g/10min |
| Shrinkage rate | | ASTM D955 | 0.50to0.80 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 118 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-2 |
| UL flame retardant rating | | UL 94 | V-2 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| transparency | | JISK7361 | 57 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | | ASTM D638 | >100 % |
| Flexural modulus | | ASTM D790 | 2260 MPa |
| tensile strength | | ASTM D638 | 61.8 MPa |
| bending strength | | ASTM D790 | 93.2 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 780 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 130 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 6.8E-05 cm/cm/°C |
| RTI Elec | | UL 746 | 80.0 °C |
| RTI Imp | | UL 746 | 80.0 °C |
| RTI Str | | UL 746 | 80.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.