LCP S475 BK210P TAIWAN POLYPLASTICS

Form：Granules | Grade：Injection grade

Properties:

Low warpageHigh mobilityheat-resistingFlame retardantenhanceGlass fiber reinforced

Typical Applications:

Electrical applicationsHome appliance components

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical applications \| Home appliance components
Properties:	Low warpage \| High mobility \| heat-resisting \| Flame retardant \| enhance \| Glass fiber reinforced

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	15	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Fracture bending strain		ISO 178	2.4	%
bending strength	23°C	ISO 178	180	Mpa
Bending modulus	23°C	ISO 178	12000	Mpa
Tensile strain	Break	ISO 527-2/1A/5	1.8	%
tensile strength	Break	ISO 527-2/1A/5	135	Mpa
Tensile modulus		ISO 527-2/1A	12300	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Spray nozzle temperature			355 to 370	°C
Processing (melt) temperature			360 to 375	°C
Mold temperature			80 to 120	°C
Injection speed			中等
Temperature at the front of the material cylinder			345 to 365	°C
Temperature in the middle of the barrel			340 to 360	°C
Temperature at the rear of the barrel			330 to 350	°C
Hopper temperature			20 to 40	°C
Suggested maximum moisture content			0.010	%
drying time			6.0	hr
drying temperature			150	°C
Back pressure			< 3.00	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	2.5E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow	ISO 11359-2	1.0E-5	cm/cm/°C
Melting temperature		ISO 11357-3	350	°C
Hot deformation temperature	8.0 MPa, Unannealed	ISO 75-2/C	213	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	305	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	Flow	ISO 294-4	0.0	%
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	0.40	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Relative permittivity	1 MHz	IEC 60250	3.70
Dissipation factor	1 MHz	IEC 60250	8.0E-3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App