Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.29 -- |
| Water absorption rate | | % | 1.5 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | | 85 -- |
| ball-indentation hardness | | MPa | 250 -- |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | HB -- |
| UL flame retardant rating | | | HB -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | MPa | 5000 -- |
| tensile strength | | MPa | 100 100 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | kJ/m² | >4.0 -- |
| Impact strength of simply supported beam without notch | | | 无断裂 -- |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ohms | >1.0E+13 >1.0E+12 |
| Volume resistivity | | ohms·cm | >1.0E+15 >1.0E+14 |
| dielectric strength | | kV/mm | 30 -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Minimum operating temperature | | °C | -40 -- |
| maximum service temperature | | °C | 110 -- |
| maximum service temperature | | °C | 170 -- |
| Heat distortion temperature | | °C | 80.0 -- |
| melting temperature | | °C | 225 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 8E-05 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 9E-05 -- |
| thermal conductivity | | W/m/K | 0.30 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.