| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | | >5.0E+9 ohms·cm |
| Dissipation Factor | | | 0.070 |
| Supporting hardness | | | 69 |
| LapShearStrength | | | 1.50 MPa |
| | | 5.63 |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| colour | | | Clear/Transparent |
| colour | | | Grey |
| density | | | 1.07 g/cm³ |
| density | | | 1.86 g/cm³ |
| density | | | 6.5到11 Pa·s |
| density | | | >2.0 hr |
| density | Pot Life | | 90 min |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| | | 26 wk |
| | | 按重量计算的混合比:10 |
| | | 按重量计算的混合比:2.0 |
| physical property | Test Condition | Test Method | Test Result |
|---|
| Particle size | | | <20.0 µm |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| WeightLossonHeating | | | 1.2 % |
| WeightLossonHeating | | | 4.5 % |
| DegradationTemperature | | | 294 °C |
| Shear Strength | | | 2.34 MPa |
| Operating | | | -55到125 °C |
| Operating | | | -55到225 °C |
| Operating | | | 9.87 MPa |
| Operating | | | 2.20 |
| WeightLossonHeating | | | 0.50 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | | <5.00 °C |
| | | 6.8E-05 cm/cm/°C |
| | | 2E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | | | 0.20 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.