ABS POLYblend PC/ABS 65FS

Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
melt mass-flow rate		ISO1133	25 g/10min
density		ISO1183	1.12 g/cm³
Shrinkage rate		ISO294-4	0.50到0.70 %
Shrinkage rate	Shrinkage rate		ISO294-4	0.50到0.70 %

flammability	Test Condition	Test Method	Test Result
Hot filament ignition temperature		IEC60695-2-13	650 °C
UL flame retardant rating		UL94	HB

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO179	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch		ISO179	无断裂
Charpy Notched Impact Strength		ISO179	16 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO179	45 kJ/m²

Mechanical properties	Test Condition	Test Method	Test Result
Tensile stress		ISO527-2	58.0 MPa
Tensile strain	Yield	ISO527-2	7.0 %
Flexural modulus		ISO178	2400 MPa
Bending stress		ISO178	95.0 MPa

Thermal performance	Test Condition	Test Method	Test Result
		ISO75-2/B	110 °C
			ISO75-2/B	111 °C
				ISO75-2/A	93.0 °C
					ISO75-2/A	100 °C
vicat		ISO306/A50	124 °C
vicat	vicat		ISO306/B50	109 °C
BallPressure Test		IEC60695-10-2	通过

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.