PC 2407 COVESTRO THAILAND

Form：Granules | Grade：Injection grade

Properties:

Low viscosityUV resistanceHigh mobilityThermal stabilityGood demolding performanc

Typical Applications:

Industrial applicationsElectrical fieldElectronic fieldAutomotive sectorcurrencycurrency

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Industrial applications \| Electrical field \| Electronic field \| Automotive sector \| currency \| currency
Properties:	Low viscosity \| UV resistance \| High mobility \| Thermal stability \| Good demolding performanc

Certificates

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
Transmittance rate	1000μm	ISO 13468-2	89.0	%
Refractive index		ISO 489	1.58	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	23°C	ISO 527-2	66.0	Mpa
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	12	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	75	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	65	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	14	kJ/m²
Bending modulus	23°C	ISO 178	2350	Mpa
bending strength	23°C	ISO 178	98.0	Mpa
Tensile creep modulus	1000Hr	ISO 899-1	1900	Mpa
Tensile modulus	23°C	ISO 527-2	2400	Mpa
Tensile creep modulus	1Hr	ISO 899-1	2200	Mpa
Elongation at Break	23°C	ISO 527-2	>50	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD	ISO 11359-2	6.5E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	6.5E-05	cm/cm/°C
Vicat softening temperature		ISO 306/B50	143	°C
Hot deformation temperature	1.80MPaAnnealed	ISO 75-2/Af	124	°C
Hot deformation temperature	Hot deformation temperature	0.45MPaUnannealed	ISO 75-2/Bf	136	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	300℃/1.2Kg	ISO 1133	19.0	cm3/10min
Water absorption rate	(23°C,24hr)	ISO 62	0.30	%
Water absorption rate	Water absorption rate	(23°C,50RH)	ISO 62	0.12	%
Shrinkage rate	TD2.0mm	ISO 294-4	0.70	%
Shrinkage rate	Shrinkage rate	MD2.0mm	ISO 294-4	0.65	%
density		ISO 1183	1.2	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	23°C	IEC 60250	9E-03	1MHz
	Dissipation factor	相对漏电起痕指数	IEC 60112	250	V
	Dissipation factor	Dissipation factor	23°C	IEC 60250	5E-04	100HZ
Dielectric constant	23°C	IEC 60250	3.00	1MHz
Surface resistivity		IEC 60093	1E+16	Ω.cm
Dielectric strength		IEC 60243-1	25	KV/mm
Volume resistivity		IEC 60093	1E+15	Ω.cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test		ISO 2039-1	116	Mpa
flame retardant performance	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL -94	HB	3.00mm
	UL flame retardant rating		UL -94	HB	6.00mm
		UL flame retardant rating		UL -94	HB	2.70mm
			UL flame retardant rating		UL -94	V-2	2.60mm
				UL flame retardant rating		UL -94	V-2	1.50mm
				UL flame retardant rating	UL flame retardant rating		UL -94	V-2	0.75mm
Extreme Oxygen Index		ISO 4589-2	27	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.