AS(SAN) 368R INEOS STYRO THAILAND

Form：Granules | Grade：Injection grade

Properties:

transparentGood stability

Typical Applications:

MonitorPenHousehold goodsElectrical appliancesToothbrush handle

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Monitor \| Pen \| Household goods \| Electrical appliances \| Toothbrush handle
Properties:	transparent \| Good stability

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
turbidity		ASTM D1003	<1.0	%
transmissivity	550nm	ASTM D1003	>89.0	%
Refractive index		ISO 489	1.569
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	18	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179	18	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	125	Mpa
Tensile creep modulus	1000hr	ISO 899-1	2800	Mpa
Tensile creep modulus	Tensile creep modulus	1hr	ISO 899-1	3500	Mpa
Tensile strain	Break,23°C	ISO 527-2	3.0	%
tensile strength	Yield,23°C	ISO 527-2	75.0	Mpa
Tensile modulus		ISO 527-2	3700	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
thermal conductivity		DIN 52612	0.17	W/m/K
Linear coefficient of thermal expansion	MD	ISO 11359-2	7E-05	cm/cm/°C
Vicat softening temperature		ISO 306/B50	106	°C
Hot deformation temperature	0.45MPa,Annealed	ISO 75-2/B	100	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	88.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate		ISO 294-4	0.30-0.70	%
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	10.0	cm3/10min
Apparent density			0.65	g/cm³
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	1MHz	IEC 60250	7E-03
Dissipation factor	Dissipation factor	100Hz	IEC 60250	4E-03
Dielectric constant	100Hz	IEC 60250	3.00
Volume resistivity		IEC 60093	1E+16	ohms·cm
Surface resistivity		IEC 60093	>1.0E+15	ohms
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test		ISO 2039-1	165	Mpa
Rockwell hardness	M-Scale		83

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.