Technical Data Sheet
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| | | 0.85到1.2 Pa·s |
| Curing Time | | | 3.0到3.5 hr |
| STORAGE STABILITY | | | 6.0到7.0 min |
| density | | | 1.14到1.18 g/cm³ |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Resin | | 按重量计算的混合比:100按容量计算的混合比:100 |
| Hardener | | 按重量计算的混合比:110按容量计算的混合比:91 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO7619 | 81到85 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO178 | 2500到3000 MPa |
| Bending stress | | ISO178 | 102到122 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | 31到45 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 78.0到84.0 °C |
| Glass Transition Temperature | | DSC | 100 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.