Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.10 g/cm³ |
| | | 600 mPa·s |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | | 87 |
| | | 86 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| PenetrationDepth | | | 210.0 µm |
| CriticalExposure | | | 24.0 mJ/cm² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | | 50.0 MPa |
| elongation | Break | | 3.0到12 % |
| elongation | | | 4.4 % |
| Flexural modulus | | | 2260 MPa |
| Flexural modulus | | | 2080 MPa |
| bending strength | | | 87.0 MPa |
| bending strength | | | 79.0 MPa |
| tensile strength | | | 51.0 MPa |
| Tensile modulus | | | 2370 MPa |
| Tensile modulus | | | 2090 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | | 30 J/m |
| Impact strength of cantilever beam gap | | | 25 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | | 58.0 °C |
| | | 117 °C |
| | | 53.0 °C |
| | | 100 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.