Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTMD1238 | 21 g/10min |
| Shrinkage rate | | 内部方法 | 0.15到0.25 % |
| Shrinkage rate | | 内部方法 | 0.25到0.50 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Dart impact equipped with measuring instruments | | ASTMD3763 | 14.2 J |
| Suspended wall beam without notch impact strength | | ASTMD4812 | 400 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strength 1 | | ASTMD638 | 81.0 Mpa |
| elongation | | ASTMD638 | 4.9 % |
| Flexural modulus | | ASTMD790 | 5030 Mpa |
| bending strength | | ASTMD790 | 124 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Arc resistance 6 | | ASTMD495 | PLC 5 |
| Compared to the Leakage Tracking Index (CTI) | | UL746 | PLC 3 |
| High arc combustion index (HAI) | | UL746 | PLC 3 |
| High Voltage Arc Traceability Rate (HVTR) | | UL746 | PLC 4 |
| Hot wire ignition (HWI) | | UL746 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| RTI | | UL746 | 130 °C |
| | ASTMD648 | 141 °C |
| | ASTMD648 | 135 °C |
| vicat | | ASTMD15255 | 144 °C |
| | ASTME831 | 2.3E-05 cm/cm/°C |
| | ASTME831 | 2.5E-05 cm/cm/°C |
| | ASTME831 | 4.9E-05 cm/cm/°C |
| | ASTME831 | 5.6E-05 cm/cm/°C |
| RTI Elec | | UL746 | 120 °C |
| RTI Imp | | UL746 | 120 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.