Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | % | 0.70 0.70 |
| Water absorption rate | | % | 1.3 1.3 |
| Shrinkage rate | | % | 1.3 1.3 |
| Shrinkage rate | | % | 0.70 0.70 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | V-2 V-2 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | MPa | 3000 2700 |
| tensile strength | | | 90.0 MPa |
| Tensile strain | | % | 6.0 6.0 |
| Tensile strain | | % | 60 |
| Flexural modulus | | MPa | 2900 2600 |
| bending strength | | MPa | 126 113 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | kJ/m² | 80 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | 1E+15 -- |
| dielectric strength | | kV/mm | 33 -- |
| dielectric constant | | | 3.30 -- |
| Dissipation Factor | | | 0.060 -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | °C | 100 85.0 |
| Heat distortion temperature | | °C | 90.0 70.0 |
| Linear coefficient of thermal expansion | | cm/cm/°C | 7.7E-05 7.7E-05 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.