EAA PRIMACOR™ 3460 DOW USA
95
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 190℃/2.16kg | ASTM D-1238 | g/10min | |
| 190℃/2.16kg | ISO 1133 | g/10min | ||
| Monomer content | % | Internal Method | ||
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238,ISO1133 | 20 | g/10min |
| Content of comonomer | 内部方法 | 9.7 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | 屈服,模压成型 | ASTMD638,ISO527-2 | 7.24 | Mpa |
| 断裂,模压成型 | ASTMD638,ISO527-2 | 16.2 | Mpa | |
| elongation | 断裂,模压成型 | ASTMD638,ISO527-2 | 580 | % |
| Tensile yield strength | Compression Molded | ASTM D-638 | Mpa | |
| Compression Molded | ISO 527-2 | Mpa | ||
| Tensile fracture strength | Compression Molded | ASTM D-638 | Mpa | |
| Compression Molded | ISO 527-2 | Mpa | ||
| Tensile strain at break | Compression Molded | ASTM D-638 | % | |
| Compression Molded | ISO 527-2 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | ASTM D-1525 | ℃ | ||
| ISO 306 | ℃ | |||
| Melting temperature | ℃ | Internal Method | ||
| vicat softening point | ASTMD1525,ISO306 | 72.2 | °C | |
| Melting temperature | 内部方法 | 95.0 | °C |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Initial sealing temperature | 内部方法 | 85.0 | °C | |
| Water vapor permeability | 38°C,90%RH | DIN53122/2 | 0.44 | g·mm/m²/atm/24hr |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Sealing starting temperature | ℃ | Internal Method | 85 | |
| Water vapor transmission rate | 38℃，90% RH | g·mm/m | DIN 53122/2 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.