| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| water content | < 0.020 | % | ||
| Shrinkage rate - flow | 3.20 mm | ASTM D955 | 0.60 到 0.80 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Non notched cantilever beam impact | 3.20 mm | ASTM D4812 | 无断裂 | |
| Tensile modulus | ASTM D638 | 2140 | Mpa | |
| tensile strength | ASTM D638 | 58.6 | Mpa | |
| elongation | 屈服 | ASTM D638 | 8.0 | % |
| Bending modulus | ASTM D790 | 2280 | Mpa | |
| bending strength | ASTM D790 | 82.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8 MPa, 未退火 | ASTM D648 | 64.4 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Static Decay | FTMS 101C 4046.1 | < 2.0 | sec | |
| Surface resistivity | -- | ESD STM11.11 | 1.0E+5 到 1.0E+9 | ohms |
| -- | ASTM D257 | 1.0E+6 到 1.0E+10 | ohms | |
| Volume resistivity | ASTM D257 | 1.0E+2 到 1.0E+5 | ohms·cm |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Injection pressure | 68.9 到 103 | Mpa | ||
| Dew Point | -40 | °C | ||
| drying temperature | 79 | °C | ||
| Processing (melt) temperature | 232 到 282 | °C | ||
| Mold temperature | 49 到 93 | °C | ||
| drying time | 4.0 | hr |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.