Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D-955 | 0.4(0.8) % |
| other | Test Condition | Test Method | Test Result |
|---|
| characteristic | | | 阻燃 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTM D-570 | 0.3(3.0) % |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| Glass Fiber Content | | | 30 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D-256 | 70(80) J/m |
| Flexural modulus | | ASTM D-790 | 12000(8500) Mpa |
| tensile strength | | ASTM D-638 | 170(140) Mpa |
| Rockwell hardness | | ASTM D-785 | 110 M Scale |
| elongation | | ASTM D-638 | 3(3) % |
| bending strength | | ASTM D-790 | 260(220) Mpa |
| elongation at break | | ASTM D638/ISO 527 | 4(3) % |
| tensile strength | | ASTM D638/ISO 527 | 160(140) kg/cm²(MPa)[Lb/in²] |
| Rockwell hardness | | ASTM D785 | 95 |
| Flexural modulus | | ASTM D638/ISO 527 | 11000(8000) % |
| bending strength | | ASTM D790/ISO 178 | 240(200) % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | ASTM D-150 | 0.012 |
| Volume resistivity | | ASTM D-257 | 10 Ω.cm |
| dielectric strength | | ASTM D-149 | 20 KV/mm |
| dielectric constant | | ASTM D-150 | 3.9 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 1.63 |
| Shrinkage rate | | ASTM D955 | 0.4(0.8) % |
| Water absorption rate | | ASTM D570/ISO 62 | 0.3(3.0) % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass transition temperature (Tg) | | | 85 °C |
| UL flame retardant rating | | UL 94 | V-0 |
| Linear coefficient of thermal expansion | | ASTM D-696 | 2.4(5.0) |
| Heat distortion temperature | | ASTM D-648 | 295 °C |
| melting temperature | | | 310 °C |
| Combustibility (rate) | | UL 94 | V-0 |
| melting temperature | | | 310 ℃（℉） |
| Linear coefficient of thermal expansion | | ASTM D696/ISO 11359 | 3.0(6.0) mm/mm.℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.