PA12

PA12 VESTAMID® L LX9102 Altuglas International of Arkema Inc.

Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C,Complete Break	ISO 179/1eA	5.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C,Partial Break	ISO 179/1eA	90 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	3.2mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.6mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	640 MPa
tensile strength	Yield	ISO 527-2	32.0 MPa
Tensile strain	Break	ISO 527-2	>50 %
Tensile strain	Tensile strain	Yield	ISO 527-2	37 %
tensile strength	Break	ISO 527-2	39.0 MPa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	120 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	55.0 °C
Vicat softening temperature	--	ISO 306/A	169 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B	136 °C
Melting temperature		ISO 11357-3	171 °C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	1.5E-04 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Saturation,23°C	ISO 62	1.5 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.50 %
Shrinkage rate	MD	ISO 294-4	1.4 %
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	1.5 %
density	23°C	ISO 1183	1.12 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
insulation resistance		IEC 60167	1E+04 ohms
Volume resistivity		IEC 60093	1E+04 ohms·cm

Supplementary Information	Test Condition	Test Method	Test Result
ISO Shortcut		ISO 1874	PA12-HIP.EHLZ.22-005

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.