HDPE BM593

Properties:
High rigidity
Resistance to stress crac
Usages:
chip
Cosmetic
Household goods
Industrial applications
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
melt mass-flow rate		ISO 1133	0.27 g/10min
melt mass-flow rate	melt mass-flow rate			26 g/10min
			200 hr

Mechanical properties	Test Condition	Test Method	Test Result
Tensile sea yield 23OC		ASTM D638	24.8 Mpa
Tensile strength yielding 23（		ISO 527	31 Mpa
Tensile strength at 23 ℃		ISO 527	28 Mpa
Elongation rate at 23 ℃		ASTM D638	650 %
	Elongation rate at 23 ℃		ISO 527	7 %
	Elongation rate at 23 ℃	Elongation rate at 23 ℃		ISO 527	700 %
Bending modulus at 23 ℃		ASTM D790	1170 Mpa
Bending modulus at 23 ℃	Bending modulus at 23 ℃		ISO 178	1550 Mpa
Cantilever beam notch impact at 23 ℃		ASTM D256	534 J/m
Cantilever beam notch impact at 23 ℃	Cantilever beam notch impact at 23 ℃		ISO 180	205 kJ/m²
Cantilever beam notch impact -30 ℃		ISO 180	50 kJ/m²

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.