Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 0.948 g/cm³ |
| Water absorption rate | | ASTM D570 | 0.030 % |
| Environmental stress cracking resistance | | ASTM D1693 | 120 hr |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 63to65 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | Break | ASTM D638 | >700 % |
| Flexural modulus | | ASTM D790 | 1170 MPa |
| Tensile modulus | | ASTM D638 | 938 MPa |
| tensile strength | Yield | ASTM D638 | 27.6 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 170to240 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 75.6 °C |
| Continuous use temperature | | | 98.9 °C |
| brittle temperature | | ASTM D746 | <-80.0 °C |
| melting temperature | | ASTM D4591 | 127 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 1.3E-4到2.0E-4 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.