PET Lighter™ S98
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Apparent density | 内部方法 | 0.88 g/cm³ | |
| water content | 内部方法 | <0 ppm | |
| Acetaldehyde | 内部方法 | <1.0 ppm | |
| Crystallinity | 内部方法 | >50 % | |
| weight | 内部方法 | 1.5 g | |
| intrinsic viscosity | 内部方法 | 0.83to0.87 dl/g |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ColorCoordinate-b | 内部方法 | <2.00 | |
| FineParticles | 内部方法 | <500 ppm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | Yield | ISO 527-2 | 55.0 MPa |
| Break | ISO 527-2 | 24.0 MPa | |
| Tensile strain | Yield | ISO 527-2 | 4.0 % |
| Tensile modulus | ISO 527-2 | 2300 MPa | |
| Tensile strain | Break | ISO 527-2 | 250 % |
| Flexural modulus | ISO 178 | 2100 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 180 | 4.5 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | 内部方法 | 247 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 8.3E-05 cm/cm/°C | |
| Glass Transition Temperature | 内部方法 | 78.0 °C | |
| vicat | ISO 306/B50 | 77.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.