HIPS 2710 BASF-YPC

Form：Granules | Grade：Impact resistant grade

Properties:

Low temperature resistancHigh temperature resistanhigh strengthHigh impact resistanceResistance to stress crac

Typical Applications:

Platesheet

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Plate \| sheet
Properties:	Low temperature resistanc \| High temperature resistan \| high strength \| High impact resistance \| Resistance to stress crac

Certificates

No Data...

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
Color			无色
characteristic			高冲击.高刚度。
Other performance	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527	1600	Mpa
machinability	Test Condition	Test Method	Test Result	Test Unit
Injection mold temperature			10-60	°C
Melt Temperature			180-240	°C
Injection molding melt temperature			180-260	°C
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate		ISO 1133	3.2	cm3/10min
density		ISO 1183	1.05	g/cm³
Water absorption rate		ISO 62	<0.1	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Elongation at Break		ASTM D638/ISO 527	40	%
bending strength		ASTM D790/ISO 178	32	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	70
Rockwell hardness	Rockwell hardness		ASTM D-785	70	L标尺
Impact strength of cantilever beam gap	23℃	ISO 180	10	kJ/m²
bending strength		ISO 178	32	Mpa
Elongation at Break		ISO 527	40	%
Tensile stress		ISO 527	21	Mpa
Charpy Notched Impact Strength	23℃	ISO 179/1eA	11	kJ/m²
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature		ASTM D1525/ISO R306	90	℃（℉）
Vicat softening temperature	Vicat softening temperature		ISO 306	90	°C
UL flame retardant rating		UL 94	HB
Hot deformation temperature	HDT	ISO 75	88	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate		ASTM D570/ISO 62	10.5	%
Shrinkage rate			0.4-0.7	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 6093	>1014	Ω.cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.