Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Resin | | 按重量计算的混合比:100 |
| | | 4.0 hr |
| Hardener | | 按重量计算的混合比:100 |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.33到1.37 g/cm³ |
| | | 0.95到1.3 Pa·s |
| Curing Time | | | 0.58到0.75 hr |
| STORAGE STABILITY | | | 5.0到7.0 min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO7619 | 82到88 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO178 | 3700到4300 MPa |
| Bending stress | | ISO178 | 65.0到75.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | 5.8到8.8 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 50.0到54.0 °C |
| Glass Transition Temperature | | TMA | 79.0 °C |
| | DIN53752 | 1E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.