PC/PTFE LNP™ LUBRICOMP™ DL-4020 BK
113
- Properties:Easy to demouldwear resistantEasy to form
- Usages:Plastic bagElectrical appliancesElectronic and Electrical Applications
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.70 到 0.90 % | |
| ASTM D955 | 0.70 到 0.90 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D638 | 53.0 Mpa | |
| elongation | ASTM D638 | 53 % | |
| Flexural modulus | ASTM D790 | 2270 Mpa | |
| bending strength | ASTM D790 | 81.0 Mpa | |
| Friction coefficient 1 | ASTM D3702 | 0.28 | |
| ASTM D3702 | 0.17 | ||
| ASTM D3702 | 2.0E+7 10^-8 mm³/N·m |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ASTM D4812 | 无断裂 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 120 °C | ||
| drying time | 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature at the rear of the barrel | 295 到 305 °C | ||
| Temperature in the middle of the barrel | 305 到 315 °C | ||
| Temperature at the front of the material cylinder | 310 到 320 °C | ||
| Processing (melt) temperature | 300 到 315 °C | ||
| Temperature | 80 到 110 °C | ||
| Back pressure | 0.200 到 0.300 Mpa | ||
| screw speed | 30 到 60 rpm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Thermal deformation temperature under load | ASTM D648 | 128 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.