PA6

PA6 SOLLAMID B 2700 FV 35 Krisoll Resinas Plásticas Ltda.

Properties:
Filler glass fiber reinforced material 35% filler by weight
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	kJ/m²	14 25

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6mm		HB --

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	23°C	MPa	10900 6000
tensile strength	23°C	MPa	170 110
elongation	Break,23°C	%	2.8 4.0
Bending modulus	23°C	MPa	9700 5200
bending strength	23°C	MPa	260 160

thermal performance	Test Condition	Test Method	Test Result
Melting temperature		°C	214to220 --
Linear coefficient of thermal expansion	MD	cm/cm/°C	2E-05 --
Hot deformation temperature	0.45MPa,Unannealed	°C	220 --
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	°C	210 --

Physical properties	Test Condition	Test Method	Test Result
density		g/cm³	1.40 --
Shrinkage rate	MD	%	0.25to0.35 --
Water absorption rate	23°C,24hr	%	0.90 --
thermal stability		°C	110to120 --

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		ohms·cm	1E+15 --
Dielectric strength		kV/mm	22 --

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale,23°C		125 112

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.