Technical Data Sheet
| other | Test Condition | Test Method | Test Result |
|---|
| characteristic | | | 刚性高.强度高 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.42 g/cm |
| Water absorption rate | | ISO 62 | 0.2 % |
| Water absorption rate | | ISO 62 | 0.75 % |
| melt mass-flow rate | | ISO 1133 | 12.07 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | ISO 2039 part 1 | 140 Mpa |
| tensile strength | | ISO 527 part 1/2 | 65 Mpa |
| elongation at break | | ISO 527 part 1/2 | 20 % |
| elongation | | ISO 527 part 1/2 | 9.0 % |
| Tensile modulus | | ISO 527 part 1/2 | 2800 Mpa |
| Flexural modulus | | ISO 178 | 2700 Mpa |
| Impact strength of simply supported beam without notch | | ISO 179 1eU | 12.0 J/cm |
| Charpy Notched Impact Strength | | ISO 179 1eA | 0.6 J/cm |
| Impact strength of simply supported beam without notch | | ISO 179 1eU | 12 J/cm |
| Charpy Notched Impact Strength | | ISO 179 1eA | 0.6 J/cm |
| Tensile creep modulus | | ISO 899 part 1 | 2400 Mpa |
| Tensile creep modulus | | ISO 899 part 1 | 1200 Mpa |
| Tensile modulus | | ASTM D638/ISO 527 | 696000 kg/cm²(MPa)[Lb/in²] |
| Flexural modulus | | ASTM D790/ISO 178 | 653000 kg/cm²(MPa)[Lb/in²] |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | IEC 60250 | 4.20 |
| dielectric constant | | IEC 60250 | 4.20 |
| dielectric strength | | IEC 60243 part 1 | 35 KV/mm |
| Dissipation Factor | | IEC 60250 | 0.008 1 MHz |
| Dissipation Factor | | IEC 60250 | 0.0025 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 1.48 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ISO 11359 part 1/2 | 110 µm/m-℃ |
| melting temperature | | ISO 3146 method C1b | 166 °C |
| Heat distortion temperature | | ISO 75 part 1/2 | 100 °C |
| vicat | | ISO 306 | 150 °C |
| vicat | | ASTM D1525/ISO R306 | 313 ℃（℉） |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.