PA6 CM1011G-15 TORAY JAPAN

Form：Granules | Grade：Injection grade

Properties:

Glass 45% reinforcedHigh modulus applicationHigh impact Glass 45% reinforcedHigh modulus applicationHigh impact

Typical Applications:

Automotive sector

Supplier(1)

Product Description

Certificates(0)

Datasheet

Alternative Model(9)

Product Description

Typical Applications:	Automotive sector
Properties:	Glass 45% reinforced \| High modulus application \| High impact \| Glass 45% reinforced \| High modulus application \| High impact

Certificates

No Data...

Technical Data Sheet

Other performance	Test Condition	Test Method	Test Result	Test Unit
filler content			无水｜45	wt%
filler content	filler content			1.9%水｜-	wt%
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	23℃，24hr	ASTM D-570	无水｜0.9	%
Water absorption rate	Water absorption rate	23℃，24hr	ASTM D-570	1.9%水｜-	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23℃，Unnotched1/8	ASTM D-256	1.9%水｜120	kg·cm/cm
Bending modulus	23℃	ASTM D-790	无水｜122000	kg/cm2
	Bending modulus	23℃	ASTM D-790	1.9%水｜72000	kg/cm2
		Bending modulus	80℃	ASTM D-790	无水｜63000	kg/cm2
			Bending modulus	80℃	ASTM D-790	1.9%水｜45000	kg/cm2
				Bending modulus	-40℃	ASTM D-790	无水｜140000	kg/cm2
				Bending modulus	Bending modulus	-40℃	ASTM D-790	1.9%水｜120000	kg/cm2
Rockwell hardness	23℃	ASTM D-785	无水｜95	M-标度
	Rockwell hardness	23℃	ASTM D-785	1.9%水｜-	M-标度
	Rockwell hardness	Rockwell hardness	23℃	ASTM D-785	无水｜121	R-标度
Elongation at Break	23℃	ASTM D-638	无水｜5	%
Elongation at Break	Elongation at Break	23℃	ASTM D-638	1.9%水｜5	%
Impact strength of cantilever beam gap	-40℃，Unnotched1/8	ASTM D-256	无水｜12.5	kg·cm/cm
	Impact strength of cantilever beam gap	-40℃，Unnotched1/8	ASTM D-256	1.9%水｜15	kg·cm/cm
		Impact strength of cantilever beam gap	-40℃，Unnotched1/8	ASTM D-256	无水｜12.5	kg·cm/cm2
			Impact strength of cantilever beam gap	-40℃，Unnotched1/8	ASTM D-256	1.9%水｜15	kg·cm/cm2
				Impact strength of cantilever beam gap	23℃，VNotched1/2	ASTM D-256	无水｜15	kg·cm/cm
					Impact strength of cantilever beam gap	23℃，VNotched1/2	ASTM D-256	1.9%水｜20	kg·cm/cm
					Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃，Unnotched1/8	ASTM D-256	无水｜98	kg·cm/cm
Shear strength	23℃	ASTM D-732	无水｜940	kg/cm2
Shear strength	Shear strength	23℃	ASTM D-732	1.9%水｜750	kg/cm2
Rockwell hardness	23℃	ASTM D-785	1.9%水｜-	R-标度
bending strength	23℃	ASTM D-790	无水｜2900	kg/cm2
	bending strength	23℃	ASTM D-790	1.9%水｜1850	kg/cm2
		bending strength	80℃	ASTM D-790	无水｜16000	kg/cm2
			bending strength	80℃	ASTM D-790	1.9%水｜-	kg/cm2
				bending strength	-40℃	ASTM D-790	无水｜3300	kg/cm2
				bending strength	bending strength	-40℃	ASTM D-790	1.9%水｜-	kg/cm2
tensile strength	23℃，Yield	ASTM D-638	无水｜2000	kg/cm2
	tensile strength	23℃，Yield	ASTM D-638	1.9%水｜1300	kg/cm2
		tensile strength	80℃，Yield	ASTM D-638	无水｜1200	kg/cm2
			tensile strength	80℃，Yield	ASTM D-638	1.9%水｜-	kg/cm2
				tensile strength	-40℃，Yield	ASTM D-638	无水｜2900	kg/cm2
				tensile strength	tensile strength	-40℃，Yield	ASTM D-638	1.9%水｜-	kg/cm2
compressive strength	23℃	ASTM D-695	无水｜1900	kg/cm2
	compressive strength	23℃	ASTM D-695	1.9%水｜-	kg/cm2
		compressive strength	80℃	ASTM D-695	无水｜1000	kg/cm2
			compressive strength	80℃	ASTM D-695	1.9%水｜-	kg/cm2
				compressive strength	-40℃	ASTM D-695	无水｜2600	kg/cm2
				compressive strength	compressive strength	-40℃	ASTM D-695	1.9%水｜-	kg/cm2
thermal performance	Test Condition	Test Method	Test Result	Test Unit
UL-94 flame retardant grade	1/32"	UL 94	无水｜HB
UL-94 flame retardant grade	UL-94 flame retardant grade	1/32"	UL 94	1.9%水｜-
Hot deformation temperature	4.6kg/cm2	ASTM D-648	无水｜225	°C
Hot deformation temperature	Hot deformation temperature	4.6kg/cm2	ASTM D-648	1.9%水｜-	°C
Melting temperature		差示扫描测热计DSC	225	°C
specific heat			无水｜0.31	Cal/g·℃
specific heat	specific heat			1.9%水｜-	Cal/g·℃
Linear coefficient of thermal expansion		ASTM D-696	无水｜2-3	×10-5cm/cm/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ASTM D-696	1.9%水｜-	×10-5cm/cm/℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D-792	无水｜1.5
density	density		ASTM D-792	1.9%水｜-
Taber abraser	1000g,CS-17	ASTM D-1044	无水｜30	mg/1000次
Taber abraser	Taber abraser	1000g,CS-17	ASTM D-1044	1.9%水｜-	mg/1000次
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	106Hz	ASTM D-150	无水｜0.02
Dissipation factor	Dissipation factor	106Hz	ASTM D-150	1.9%水｜0.06
Dielectric strength	1/8"	ASTM D-149	无水｜19	KV/mm
Dielectric strength	Dielectric strength	1/8"	ASTM D-149	1.9%水｜15	KV/mm
Dielectric constant	106Hz	ASTM D-150	无水｜4.2
	Dielectric constant	106Hz	ASTM D-150	1.9%水｜4.5
		Dielectric constant	103Hz	ASTM D-150	无水｜4.9
		Dielectric constant	Dielectric constant	103Hz	ASTM D-150	1.9%水｜7.4
Volume resistivity		ASTM D-257	无水｜1015	Ω.cm
Volume resistivity	Volume resistivity		ASTM D-257	1.9%水｜1012	Ω.cm
Dissipation factor	50Hz	ASTM D-150	无水｜0.03
Dissipation factor	Dissipation factor	50Hz	ASTM D-150	1.9%水｜0.16
Arc resistance	1/8"	ASTM D-495	无水｜104	S
Arc resistance	Arc resistance	1/8"	ASTM D-495	1.9%水｜119	S

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.