Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.48 -- |
| Shrinkage rate | | % | 0.20to0.30 -- |
| Water absorption rate | | % | 0.90 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | | 125 115 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | HB -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | MPa | 11500 6500 |
| tensile strength | | MPa | 185 120 |
| elongation | Break | % | 2.5 3.5 |
| Flexural modulus | | MPa | 10200 6000 |
| bending strength | | MPa | 280 175 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | J/m | 130 200 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | 1E+15 -- |
| dielectric strength | | kV/mm | 22 -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Continuous use temperature | | °C | 115to125 -- |
| melting temperature | | °C | 214to220 -- |
| Heat distortion temperature | | °C | 220 -- |
| Heat distortion temperature | | °C | 215 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 2E-05 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.