PP Homopolymer TOTAL Polypropylene PPH 4026 TOTAL

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
turbidity	50.0μm,铸造薄膜	ISO 14782	14	%
gloss	45°,50.0μm,铸造薄膜	ASTM D2457	51
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ISO 180	5.0	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179	6.0	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus		ISO 178	2000	MPa
Tensile strain	Yield	ISO 527-2	9.0	%
tensile strength	Yield	ISO 527-2	39.0	MPa
Tensile modulus		ISO 527-2	2050	MPa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature		ISO 3146	165	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	0.905	g/cm³
melt mass-flow rate	230°C/2.16kg	ISO 1133	3.0	g/10min
Apparent density		ISO 60	0.53	g/cm³
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale	ISO 2039-2	95
film	Test Condition	Test Method	Test Result	Test Unit
Elmendorf tear strength	TD:50.0μm	ISO 6383-2	88.0	kN/m
Elmendorf tear strength	Elmendorf tear strength	MD:50.0μm	ISO 6383-2	6.0	kN/m
Dart impact	50μm,铸造薄膜	ISO 7765-1	80	g
elongation	TD:Break,50μm,铸造薄膜	ISO 527-3	580	%
elongation	elongation	MD:Break,50μm,铸造薄膜	ISO 527-3	470	%
tensile strength	TD:Break,50μm,铸造薄膜	ISO 527-3	35.0	MPa
	tensile strength	MD:Break,50μm,铸造薄膜	ISO 527-3	62.0	MPa
		tensile strength	TD:Yield,50μm,铸造薄膜	ISO 527-3	29.0	MPa
		tensile strength	tensile strength	MD:Yield,50μm,铸造薄膜	ISO 527-3	31.0	MPa
film thickness			50	µm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.