PC/ABS CX7110 BK SABIC INNOVATIVE JAPAN

Form：Granules | Grade：Injection grade

Properties:

Low temperature resistancHigh sliding

Typical Applications:

Electronic and electrical accessoriesAutomotive components

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electronic and electrical accessories \| Automotive components
Properties:	Low temperature resistanc \| High sliding

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	10	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	15	kJ/m²
Dart impact	23°C, Total Energy	ASTM D3763	63.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.75 mm	UL 94	V-2
	UL flame retardant rating	1.0 mm	UL 94	V-1
		UL flame retardant rating	1.2 mm	UL 94	V-0
		UL flame retardant rating	UL flame retardant rating	1.8 mm	UL 94	5VB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	--2	ASTM D638	2900	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2700	Mpa
tensile strength	Yield3	ASTM D638	64.0	Mpa
	tensile strength	Yield	ISO 527-2/50	61.0	Mpa
		tensile strength	Break3	ASTM D638	54.0	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	51.0	Mpa
elongation	Yield3	ASTM D638	4.0	%
	elongation	Yield	ISO 527-2/50	4.0	%
		elongation	Break3	ASTM D638	90	%
		elongation	elongation	Break	ISO 527-2/50	90	%
Bending modulus	50.0 mm Span4	ASTM D790	2700	Mpa
Bending modulus	Bending modulus	--5	ISO 178	2500	Mpa
bending strength	--5,6	ISO 178	100	Mpa
bending strength	bending strength	Yield, 50.0 mm Span4	ASTM D790	100	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			80 to 90	°C
drying time			3.0 to 4.0	hr
Suggested maximum moisture content			0.040	%
Suggested injection volume			30 to 80	%
Temperature at the rear of the barrel			220 to 255	°C
Temperature in the middle of the barrel			220 to 265	°C
Temperature at the front of the material cylinder			245 to 275	°C
Spray nozzle temperature			245 to 275	°C
Processing (melt) temperature			245 to 275	°C
Mold temperature			60 to 80	°C
Back pressure			0.300 to 0.700	Mpa
Screw speed			40 to 70	rpm
Exhaust hole depth			0.038 to 0.076	mm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	94.0	°C
	Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	98.0	°C
		Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	84.0	°C
			Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	90.0	°C
			Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9	ISO 75-2/Af	84.0	°C
Vicat softening temperature	--	ASTM D152510	102	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	103	°C
Ball Pressure Test	73 to 77°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.5E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.5E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	7.5E-5	cm/cm/°C
thermal conductivity		ISO 8302	0.20	W/m/K
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	260°C/2.16 kg	ASTM D1238	22	g/10 min
Melt Volume Flow Rate (MVR)	260°C/2.16 kg	ISO 1133	21.0	cm3/10min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.40 - 0.60	%
Water absorption rate	Saturation, 23°C	ISO 62	0.20	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.10	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.