Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO 62 | 2.4 % |
| Water absorption rate | | ISO 62 | 7.8 % |
| Shrinkage rate | | ISO 294-4 | 0.45 % |
| Shrinkage rate | | ISO 294-4 | 0.80 % |
| density | | ISO 1183 | 1.22 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ISO Shortcut | | ISO 1874 | PA6-HI.MHR.-050N.GF15 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 70 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 13 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Break | ISO 527-2/5 | 4.5 % |
| tensile strength | Break | ISO 527-2/5 | 95.0 MPa |
| Tensile modulus | | ISO 527-2/1 | 5200 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ISO 11357-3 | 222 °C |
| Heat distortion temperature | | ISO 75-2/A | 180 °C |
| Heat distortion temperature | | ISO 75-2/B | 200 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare