PPA HTN 51G45HSLR BK DUPONT USA

Form：Granules

Properties:

High temperature resistanHigh impact resistanceLow temperature resistancFiller: Glass fiber reinf45% filler by weight

Typical Applications:

Automotive interior parts

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive interior parts
Properties:	High temperature resistan \| High impact resistance \| Low temperature resistanc \| Filler: Glass fiber reinf \| 45% filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23℃	kJ/m²	4.178to19.964
flammability	Test Condition	Test Method	Test Result	Test Unit
Extreme Oxygen Index		%	23to25
Burning wire flammability index		°C	743to960
Hot filament ignition temperature		°C	721to926
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
shear strength	23℃		88.28to107.59	MPa
Yield, 23 ℃			102.76to362.76	MPa
Poisson's ratio	23℃		0.41
compressive strength	23℃		142.76to196.55	MPa
Yield, 23 ℃		%	1.4to2.5
Fracture, 23 ℃		%	1.5to3.1
Fracture, 23 ℃	Fracture, 23 ℃		%	1.0to2.5
Tensile modulus	摩擦系数		0.15to0.52
Yield, 23 ℃			68.97to250.34	MPa
Fracture, 23 ℃			131.72to400.0	MPa
Fracture, 23 ℃	Fracture, 23 ℃			162.76to199.31	MPa
Yield, 23 ℃		%	1.5to2.6
Yield, 23 ℃	Yield, 23 ℃			12.62to270.34	MPa
Fracture, 23 ℃			108.28to262.76	MPa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
transverse		mm/mm/°C	68.6E-5-127.0E-5
1.8MPa, annealed		°C	283to300
transverse		mm/mm/°C	63.5E-5-177.8E-5
0.45MPa, unannealed		°C	273to312
RTI Imp		°C	118to150
RTI Elec		°C	140to150
flow		mm/mm/°C	38.1E-5-50.8E-5
1.8MPa, unannealed		°C	249to304
flow		mm/mm/°C	185.4E-5-25.4E-5
flow	flow		mm/mm/°C	195.6E-5-25.4E-5
Vicat softening temperature		°C	258to313
8.0Mpa, unannealed		°C	165to230
1.8MPa, unannealed		°C	247to292
0.45MPa, annealed		°C	296to320
0.45MPa, unannealed		°C	275to308
RTI		°C	119to150
Continuous use temperature		°C	140to186
Physical properties	Test Condition	Test Method	Test Result	Test Unit
23℃,24hr		%	0.30to0.51
Balance, 23 ℃, 50% RH		%	0.21to1.2
Lateral flow: 23 ℃	Across Flow, 23℃	mm/mm	119.4E-3-0.254
23℃,24hr		%	0.12to0.30
Flow: 23 ℃	Flow,23℃	mm/mm	48.3E-3-129.5E-3
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	23℃		125

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.