PP PPB-M02D SINOPEC MAOMING

202

Form：Granules | Grade：Injection grade

Properties:

High mobilityHigh impact resistance

Typical Applications:

Plastic barrelWashing machine

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Plastic barrel \| Washing machine
Properties:	High mobility \| High impact resistance

Certificates

No Data...

Technical Data Sheet

Other performance	Test Condition	Test Method	Test Result	Test Unit
ash content			合格品｜≤0.05	%(m/m)
	ash content			一级品｜≤0.03	%(m/m)
	ash content	ash content			优级品｜≤0.02	%(m/m)
Color particles			合格品｜≤20	粒/kg树脂
	Color particles			一级品｜≤10	粒/kg树脂
	Color particles	Color particles			优级品｜≤5	粒/kg树脂
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	230℃,2.16kg		合格品｜1.0-2.2	g/10min
	melt mass-flow rate	230℃,2.16kg		一级品｜1.4-2.2	g/10min
	melt mass-flow rate	melt mass-flow rate	230℃,2.16kg		优级品｜1.6-2.0	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	-20℃		优级品｜≥4.0	kJ/m²
Rockwell hardness			合格品｜≥75	R
	Rockwell hardness			一级品｜≥75	R
	Rockwell hardness	Rockwell hardness			优级品｜≥75	R
tensile strength	Yield		合格品｜≥20.0	Mpa
	tensile strength	Yield		一级品｜≥21.0	Mpa
	tensile strength	tensile strength	Yield		优级品｜≥22.5	Mpa
Impact strength of cantilever beam gap	-20℃		合格品｜≥3.0	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-20℃		一级品｜≥3.3	kJ/m²
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature			合格品｜≥135	°C
	Vicat softening temperature			一级品｜≥135	°C
	Vicat softening temperature	Vicat softening temperature			优级品｜≥135	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.