Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | % | 1.1 1.1 |
| Water absorption rate | | % | 1.2 1.2 |
| Water absorption rate | | % | 1.9 1.9 |
| Shrinkage rate | | % | 1.5 1.5 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | | 116 97 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | V-0 V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | MPa | 3100 1800 |
| Tensile stress | | MPa | 77.0 41.0 |
| Tensile strain | | % | 3.4 4.0 |
| Flexural modulus | | MPa | 3000 1500 |
| Bending stress | | MPa | 110 60.0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | kJ/m² | 35 51 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | 1E+16 -- |
| dielectric strength | | kV/mm | 25 -- |
| dielectric constant | | | 3.00 -- |
| Dissipation Factor | | | 0.010 -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | °C | 170 -- |
| | °C | 66.0 -- |
| | cm/cm/°C | 1E-04 1E-04 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare