Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.27 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.20to0.50 % |
| Water absorption rate | | ASTM D570 | 0.13 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 105 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ASTM D1003 | 90.0 % |
| Haze ratio | | ASTM D1003 | <1.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ASTM D790 | 71.0 MPa |
| bending strength | | ISO 178 | 69.0 MPa |
| tensile strength | | ASTM D638 | 50.0 MPa |
| tensile strength | Yield | ISO 527-2/50 | 50.0 MPa |
| tensile strength | | ASTM D638 | 26.0 MPa |
| tensile strength | Break | ISO 527-2/50 | 26.0 MPa |
| elongation | | ASTM D638 | 4.5 % |
| elongation | Yield | ISO 527-2/50 | 4.5 % |
| elongation | | ASTM D638 | 120 % |
| elongation | Break | ISO 527-2/50 | 120 % |
| Flexural modulus | | ASTM D790 | 2150 MPa |
| Flexural modulus | | ISO 178 | 2050 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 85 J/m |
| Impact strength of cantilever beam gap | | ISO 180 | 7.9 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 70.0 °C |
| Heat distortion temperature | | ASTM D648 | 62.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.