TPV 5775B TEKNOR APEX BELGIUM

Form：Granules | Grade：Weather resistant grade

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	HB
elastomer	Test Condition	Test Method	Test Result	Test Unit
tensile strength	横向Flow:100%Strain	ASTM D412	3.20	Mpa
	tensile strength	Flow:100%Strain	ASTM D412	4.90	Mpa
		tensile strength	横向Flow:100%Strain	ISO 37	3.20	Mpa
			tensile strength	Flow:100%Strain	ISO 37	4.90	Mpa
				tensile strength	Break	ASTM D412	8.48	Mpa
					tensile strength	Flow:Break	ASTM D412	7.31	Mpa
						tensile strength	Break	ISO 37	8.50	Mpa
						tensile strength	tensile strength	Flow:Break	ISO 37	7.30	Mpa
elongation	Break	ASTM D412	590	%
	elongation	Flow:Break	ASTM D412	340	%
		elongation	Break	ISO 37	590	%
		elongation	elongation	Flow:Break	ISO 37	340	%
tear strength	横向Flow	ASTM D624	35.0	kN/m
tear strength	tear strength	横向Flow	ISO 34-1	35	kN/m
Permanent compression deformation	23°C,22hr	ASTM D395	23	%
	Permanent compression deformation	70°C,22hr	ASTM D395	32	%
		Permanent compression deformation	125°C,70hr	ASTM D395	47	%
			Permanent compression deformation	23°C,22hr	ISO 815	23	%
				Permanent compression deformation	70°C,22hr	ISO 815	32	%
				Permanent compression deformation	Permanent compression deformation	125°C,70hr	ISO 815	47	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI Elec		UL 746	50.0	°C
RTI Imp		UL 746	50.0	°C
RTI Str		UL 746	50.0	°C
hardness	Test Condition	Test Method	Test Result	Test Unit
Shore hardness	ShoreA,5Sec,挤塑	ASTM D2240	72
	Shore hardness	ShoreA,5Sec,Injection	ASTM D2240	75
		Shore hardness	ShoreA,5Sec,挤塑	ISO 868	72
		Shore hardness	Shore hardness	ShoreA,5Sec,Injection	ISO 868	75
aging	Test Condition	Test Method	Test Result	Test Unit
Change rate of hardness (Shore) in the air	ShoreA,135°C,1000hr	ASTM D573	3.0
	Change rate of hardness (Shore) in the air	ShoreA,150°C,168hr	ASTM D573	2.0
		Change rate of hardness (Shore) in the air	ShoreA,135°C,1000hr	ISO 188	3.0
		Change rate of hardness (Shore) in the air	Change rate of hardness (Shore) in the air	ShoreA,150°C,168hr	ISO 188	2.0
Volume change	125°C,70hr,在IRM903油中	ASTM D471	88	%
Volume change	Volume change	125°C,70hr,在IRM903油中	ISO 1817	88	%
Change rate of tensile strength in air	150°C,168hr，Across Flow	ASTM D573	-10	%
	Change rate of tensile strength in air	100%Strain,150°C,168hr，Across Flow	ASTM D573	2.0	%
		Change rate of tensile strength in air	135°C,1000hr，Across Flow	ISO 188	-8.0	%
			Change rate of tensile strength in air	100%Strain135°C,1000hr，Across Flow	ISO 188	4.0	%
				Change rate of tensile strength in air	150°C,168hr，Across Flow	ISO 188	-10	%
				Change rate of tensile strength in air	Change rate of tensile strength in air	100%Strain150°C,168hr，Across Flow	ISO 188	2.0	%
Change rate of ultimate elongation in air	135°C,1000hr，Across Flow	ASTM D573	-7.0	%
Change rate of ultimate elongation in air	Change rate of ultimate elongation in air	150°C,168hr，Across Flow	ASTM D573	-11	%
Tensile stress change rate	135°C,1000hr，Break	ISO 188	-7.0	%
Tensile stress change rate	Tensile stress change rate	150°C,168hr，Break	ISO 188	-11	%
Change rate of tensile strength in air	135°C,1000hr，Across Flow	ASTM D573	-8.0	%
Change rate of tensile strength in air	Change rate of tensile strength in air	100%Strain,135°C,1000hr，Across Flow	ASTM D573	4.0	%
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
Apparent viscosity	200°C，剪切,毛细管法, @206/s	ISO 11443	330	Pa·s
Apparent viscosity	Apparent viscosity	200°C，剪切,毛细管法, @206/s	ASTM D3835	330	Pa·s

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.