Rubber RTV-2 P-125 Silicones, Inc.
0
CompareTechnical Data Sheet
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Viscosity | 16to24 hr | ||
| Pot Life | 60to120 min | ||
| Color | Translucent | ||
| Viscosity | 1.0to2.0 Pa·s | ||
| 160to180 Pa·s | |||
| Color | Clear/Transparent |
| Cured Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore hardness | 36to44 | ||
| 36to44 | |||
| tensile strength | ASTM D412 | 4.48to5.17 MPa | |
| elongation | Break | ASTM D412 | 200to300 % |
| tear strength | ASTM D624 | 13.1to18.4 kN/m | |
| dielectric strength | 20 kV/mm | ||
| relative permittivity | 2.90 | ||
| Volume resistivity | 1E+15 ohms·cm | ||
| Coverage-Cured | 0.925 cm³/g | ||
| Dissipation Factor | 3E-03 |
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | 1.09 g/cm³ |
| thermosetting | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Thermosetting components | Resin | 按容量计算的混合比:100按重量计算的混合比:10 | |
| Hardener | 按容量计算的混合比:11按重量计算的混合比:1.0 | ||
| Shelf Life | 26 wk | ||
| 90000to110000 cP |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Usage temperature | -51-316 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.