Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Melt volume flow rate | | cm³/10min | 0.04到0.05 |
| Flow: | | mm/mm | 152.4E-3到172.7E-3 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | % | 88.9到93.1 |
| Haze ratio | | % | 0.20到3.1 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | mm/min | 38.1到53.34 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| yield | | Mpa | 24.41到54.0 |
| yield | | Mpa | 1.03到33.45 |
| Nominal tensile fracture strain | | % | 2.5到500 |
| fracture | | Mpa | 14.0到64.0 |
| fracture | | % | 30到260 |
| yield | | % | 2.0到2.1 |
| yield | | Mpa | 4.0到51.03 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | J/m | 0.007到0.037 |
| Dart impact equipped with measuring instruments | | N.m | 47.17到3256.64 |
| Charpy Notched Impact Strength | | kJ/m² | 0.353到2.182 |
| aging | Test Condition | Test Method | Test Result |
|---|
| Resistant to continuous maximum temperature | | °C | 150到170 |
| Test Condition | Test Method | Test Result |
|---|
| yield | | Mpa | 1.7到33.03 |
| fracture | | % | 400到890 |
| compression set | | % | 18到36 |
| fracture | | Mpa | 3.97到20.34 |
| fracture | | % | 550到850 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| brittle temperature | | °C | -60到-59 |
| | °C | 59到62 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare