PP AP3AW EXXONMOBIL SINGAPORE

Form：Granules | Grade：Injection grade

Properties:

Low warpageHigh rigidityHigh impact resistanceMiddle flowLight resistance

Typical Applications:

Battery boxEngine hood partsAutomotive sectorApplication in the automotive fieldParts under the hood of a car

Supplier(1)

Product Description

Certificates(2)

Datasheet

Product Description

Typical Applications:	Battery box \| Engine hood parts \| Automotive sector \| Application in the automotive field \| Parts under the hood of a car
Properties:	Low warpage \| High rigidity \| High impact resistance \| Middle flow \| Light resistance

Certificates

TDS

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	-29°C,3.18mm	ASTM D5420	18.1	J
Impact strength of cantilever beam gap	23°C	ISO 180/1A	8.8	kJ/m²
	Impact strength of cantilever beam gap	-18°C	ISO 180/1A	4.5	kJ/m²
		Impact strength of cantilever beam gap	-40°C	ISO 180/1A	3.4	kJ/m²
			Impact strength of cantilever beam gap	23°C	ASTM D256A	90	J/m
			Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-18°C	ASTM D256A	35	J/m
Charpy Notched Impact Strength	23°C	ISO 179/1eA	9.9	kJ/m²
	Charpy Notched Impact Strength	0°C	ISO 179/1eA	4.9	kJ/m²
		Charpy Notched Impact Strength	-20°C	ISO 179/1eA	3.9	kJ/m²
		Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	3.3	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus	--6	ISO 178	1340	Mpa
	Bending modulus	1%Secant5	ASTM D790B	1520	Mpa
	Bending modulus	Bending modulus	1%Secant4	ASTM D790A	1340	Mpa
elongation	Yield	ISO 527-2/50	5.7	%
elongation	elongation	Yield3	ASTM D638	5.6	%
tensile strength	Yield	ISO 527-2/50	25.7	Mpa
tensile strength	tensile strength	Yield3	ASTM D638	27.1	Mpa
Tensile modulus		ISO 527-2/1	1500	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	53.4	°C
	Hot deformation temperature	0.45MPa,Annealed	ASTM D648	116	°C
		Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/Bf	92.5	°C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	99.4	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	230°C/2.16kg	ASTM D1238	10	g/10min
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness		ASTM D785	96

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.