PA66 21SPC ASCEND USA

610

Form：Granules | Grade：Injection grade

Supplier(7)

Product Description

Certificates(2)

Datasheet

Alternative(13)

Product Description

Certificates

MSDS

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ISO 180	6.0	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180	5.0	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength	23°C	ISO 179/1eA	6.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	5.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.71 mm	UL 94	V-2
UL flame retardant rating	UL flame retardant rating	0.40 mm	UL 94	V-2
Burning wire flammability index	1.5 mm	IEC 60695-2-12	960	°C
UL flame retardant rating	1.5 mm	UL 94	V-2
UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	V-2
Burning wire flammability index	0.40 mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	0.71 mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	Burning wire flammability index	3.0 mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	0.40 mm	IEC 60695-2-13	825	°C
	Hot filament ignition temperature	0.71 mm	IEC 60695-2-13	850	°C
		Hot filament ignition temperature	1.5 mm	IEC 60695-2-13	850	°C
		Hot filament ignition temperature	Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	850	°C
Extreme Oxygen Index		ISO 4589-2	25	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Poisson's ratio		ISO 527	0.40
bending strength	23°C	ISO 178	80.0	Mpa
Bending modulus	23°C	ISO 178	2900	Mpa
Nominal tensile fracture strain	23°C	ISO 527-2	25	%
Tensile strain	Yield, 23°C	ISO 527-2	5.0	%
tensile strength	Break, 23°C	ISO 527-2	55.0	Mpa
tensile strength	tensile strength	Yield, 23°C	ISO 527-2	82.0	Mpa
Tensile modulus	23°C	ISO 527-2	3100	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Mold temperature			65 to 95	°C
Processing (melt) temperature			285 to 300	°C
Spray nozzle temperature			280 to 300	°C
Temperature at the front of the material cylinder			280 to 290	°C
Temperature in the middle of the barrel			270 to 285	°C
Temperature at the rear of the barrel			260 to 280	°C
Suggested maximum material return ratio			50	%
drying time			1.0 to 3.0	hr
drying temperature			< 70	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	Across Flow : 23 to 55°C	ISO 11359-2	1.0E-4	cm/cm/°C
RTI Elec	0.40 mm	UL 746	130	°C
Linear coefficient of thermal expansion	Flow : 23 to 55°C	ISO 11359-2	1.0E-4	cm/cm/°C
Melting temperature		ISO 11357-3	260	°C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	70.0	°C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	200	°C
RTI Elec	0.71 mm	UL 746	130	°C
	RTI Elec	1.5 mm	UL 746	130	°C
	RTI Elec	RTI Elec	3.0 mm	UL 746	130	°C
RTI Imp	0.40 mm	UL 746	75.0	°C
	RTI Imp	0.71 mm	UL 746	75.0	°C
		RTI Imp	1.5 mm	UL 746	75.0	°C
		RTI Imp	RTI Imp	3.0 mm	UL 746	75.0	°C
RTI	0.40 mm	UL 746	75.0	°C
	RTI	0.71 mm	UL 746	85.0	°C
		RTI	1.5 mm	UL 746	85.0	°C
		RTI	RTI	3.0 mm	UL 746	85.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Outdoor applicability	全部	UL 746C	f2
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	2.4	%
Water absorption rate	Water absorption rate	24 hr, 23°C	ISO 62	1.2	%
Shrinkage rate	Flow : 23°C, 2.00 mm	ISO 294-4	1.8	%
Shrinkage rate	Shrinkage rate	横向Flow : 23°C, 2.00 mm	ISO 294-4	1.7	%
density		ISO 1183	1.14	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity	0.750 mm	IEC 60093	1.0E+13	ohms·cm
Dielectric strength	1.00 mm	IEC 60243	26	KV/mm
Arc resistance	3.00 mm	ASTM D495	PLC 5
Compared to the anti leakage trace index	3.00 mm	IEC 60112	PLC 0
High arc combustion index	0.40 mm	UL 746	PLC 1
	High arc combustion index	0.71 mm	UL 746	PLC 0
		High arc combustion index	1.5 mm	UL 746	PLC 0
		High arc combustion index	High arc combustion index	3.0 mm	UL 746	PLC 0
High voltage arc tracing rate		UL 746	PLC 0
Hot wire ignition	0.40 mm	UL 746	PLC 4
	Hot wire ignition	0.71 mm	UL 746	PLC 4
		Hot wire ignition	1.5 mm	UL 746	PLC 3
		Hot wire ignition	Hot wire ignition	3.0 mm	UL 746	PLC 2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PA66 21SPC ASCEND USA

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index