PPO(PPE)+PS+PP

PPO(PPE)+PS+PP NORYL PPX™ PPX7110 resin SABIC

Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C,TotalEnergy	ASTM D3763	38.0 J
Dart impact	Dart impact	-30°C,TotalEnergy	ASTM D3763	27.8 J
Impact strength of cantilever beam gap	23°C	ASTM D256	440 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ASTM D256	150 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.52mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	1340 MPa
bending strength	Yield,50.0mmSpan	ASTM D790	51.7 MPa
Bending modulus	50.0mmSpan	ASTM D790	1550 MPa
elongation	Break	ASTM D638	200 %
elongation	elongation	Yield	ASTM D638	6.5 %
tensile strength	Break	ASTM D638	32.4 MPa
tensile strength	tensile strength	Yield	ASTM D638	35.9 MPa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	113 °C
RTI Elec		UL 746	50.0 °C
Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	1.1E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	8.1E-05 cm/cm/°C
Vicat softening temperature		ASTM D15256	139 °C
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	77.2 °C
RTI		UL 746	50.0 °C
RTI Imp		UL 746	50.0 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD：3.20mm	Internal Method	0.80to1.2 %
melt mass-flow rate	260°C/5.0kg	ASTM D1238	11 g/10min
density		ASTM D792	0.968 g/cm³

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.