Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183/A | 0.990 g/cm³ |
| Melt volume flow rate | | ISO 1133 | 6.00 cm³/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 76 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Hot filament ignition temperature | | IEC 60695-2-13 | 960 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 40 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ISO 527-2 | 24.0 MPa |
| tensile strength | Break | ISO 527-2 | 20.0 MPa |
| Tensile strain | Break | ISO 527-2 | 40 % |
| Flexural modulus | | ISO 178 | 2000 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 2.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 17 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 2.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/Af | 66.0 °C |
| vicat | | ISO 306/A50 | 151 °C |
| Ball pressure temperature | | IEC 60335-1 | 140 °C |
| melting temperature | | ISO 3146 | 167 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.