PC LEXAN™ EXL1414 GY7D569L
132
- Properties:ProcessabilityModerate liquidityDuctilitycopolymerGood demolding performanc
- Usages:Electrical applicationsHome appliance componentsBottle cap
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.18 g/cm³ | |
| ISO 1183 | 1.19 g/cm³ | ||
| melt mass-flow rate | ASTM D1238 | 10 g/10min | |
| Melt volume flow rate | ISO 1133 | 9.00 cm3/10min | |
| Shrinkage rate | 内部方法 | 0.40-0.80 % | |
| 内部方法 | 0.40-0.80 % | ||
| Water absorption rate | ISO 62 | 0.35 % | |
| ISO 62 | 0.15 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 89 | |
| ASTM D785 | 121 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot filament ignition temperature | IEC 60695-2-13 | 875 °C | |
| IEC 60695-2-13 | 875 °C | ||
| UL flame retardant rating | UL 94 | HB | |
| Burning wire flammability index | IEC 60695-2-12 | 850 °C | |
| IEC 60695-2-12 | 960 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ISO 180/1U | NoBreak | |
| ISO 180/1U | NoBreak | ||
| Dart impact | ASTM D3763 | 70.0 J | |
| Charpy Notched Impact Strength | ISO 179/1eA | 65 kJ/m² | |
| ISO 179/1eA | 70 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | NoBreak | |
| ISO 179/1eU | NoBreak | ||
| Impact strength of cantilever beam gap | ASTM D256 | 770 J/m | |
| ASTM D256 | 870 J/m | ||
| ISO 180/1A | 60 kJ/m² | ||
| ISO 180/1A | 70 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | ISO 178 | 85.0 Mpa | |
| ASTM D790 | 92.4 Mpa | ||
| Tensile modulus | ASTM D638 | 2020 Mpa | |
| ISO 527-2/1 | 2150 Mpa | ||
| tensile strength | ASTM D638 | 55.5 Mpa | |
| ISO 527-2/50 | 57.0 Mpa | ||
| ASTM D638 | 50.3 Mpa | ||
| ISO 527-2/50 | 60.0 Mpa | ||
| elongation | ASTM D638 | 6.0 % | |
| Tensile strain | ISO 527-2/50 | 6.0 % | |
| elongation | ASTM D638 | 98 % | |
| Tensile strain | ISO 527-2/50 | 120 % | |
| Flexural modulus | ASTM D790 | 2230 Mpa | |
| ISO 178 | 2250 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | >1.0E+15 ohms | |
| Volume resistivity | ASTM D257 | >1.0E+15 ohms·cm | |
| dielectric strength | ASTM D149 | 16 KV/mm | |
| dielectric constant | ASTM D150 | 2.68 | |
| ASTM D150 | 2.64 | ||
| Dissipation Factor | ASTM D150 | 1.2E-03 | |
| ASTM D150 | 9.3E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 139 °C | |
| ISO 75-2/Be | 140 °C | ||
| ASTM D648 | 124 °C | ||
| ISO 75-2/Ae | 128 °C | ||
| vicat | ASTM D152510 | 145 °C | |
| ISO 306/B50 | 145 °C | ||
| ISO 306/B120 | 146 °C | ||
| ball-indentation hardness | IEC 60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | ASTME831 | 7E-05 cm/cm/°C | |
| ISO 11359-2 | 7.2E-05 cm/cm/°C | ||
| ASTME831 | 7.5E-05 cm/cm/°C | ||
| ISO 11359-2 | 7.2E-05 cm/cm/°C | ||
| RTI Elec | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 120 °C | |
| RTI Str | UL 746 | 125 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.