PBT TAROLOX 10 Taro Plast S.p.A.

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179	6.0	kJ/m²
Impact strength of cantilever beam gap	-20°C,3.20mm	ASTMD256	30	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.20mm	ASTMD256	50	J/m
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.6mm	UL 94	HB
Hot filament ignition temperature	2.0mm	IEC 60695-2-13	750	°C
Extreme Oxygen Index		ASTM D2863	22	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	Break	ASTM D790	70.0	MPa
	bending strength	Yield	ASTM D790	80.0	MPa
		bending strength	--3	ISO 178	80.0	MPa
		bending strength	bending strength	--2	ISO 178	70.0	MPa
Bending modulus		ASTMD790	2300	MPa
elongation	Break	ASTMD638	>100	%
tensile strength	Break	ASTMD638	50.0	MPa
tensile strength	tensile strength	Yield	ASTMD638	55.0	MPa
Tensile modulus		ASTMD638	2500	MPa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	--	ASTMD152510	180	°C
Linear coefficient of thermal expansion	MD：-30to30°C	ASTM D696	1E-04	cm/cm/°C
Melting temperature		ASTMD211	220to225	°C
Ball Pressure Test	165°C	VDE0470	通过
Vicat softening temperature	--	ASTMD15259	200	°C
Hot deformation temperature	0.45MPa,Unannealed	ASTMD648	160	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTMD648	60.0	°C
Continuous use temperature	--5	IEC 60216	90.0	°C
	Continuous use temperature	--6	IEC 60216	120	°C
		Continuous use temperature	--7	IEC 60216	130	°C
		Continuous use temperature	Continuous use temperature	--8	IEC 60216	160	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
GranuleHumidity		Internal Method	<0.050	%
Water absorption rate	Saturation,23°C	ISO 62	0.50	%
	Water absorption rate	Saturation	ASTM D570	0.50	%
	Water absorption rate	Water absorption rate	23°C,24hr	ASTMD570	0.080	%
Shrinkage rate	TD	ASTM D955	1.6to1.8	%
Shrinkage rate	Shrinkage rate	MD	ASTM D955	1.6to1.8	%
melt mass-flow rate	250°C/1.2kg	ASTMD1238	20	g/10min
density		ASTMD792	1.30to1.32	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 0
Dielectric strength	2.00mm	ASTM D149	18	kV/mm
Volume resistivity		ASTM D257	>1.0E+15	ohms·cm
Compared to the anti leakage trace index	SolutionB	IEC 60112	PLC 2
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.