Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Particle size | | | <45.0 µm |
| Ionic type | | | 131 ppm |
| Ionic type | | | 93 ppm |
| Ionic type | | | 9 ppm |
| Ionic type | | | 18 ppm |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| shelf-life | | | 52 wk |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| Curing Time | | | 1.0 hr |
| STORAGE STABILITY | | | 4300 min |
| colour | | | Silver |
| density | | | 3.02 g/cm³ |
| | | 1.4到1.9 Pa·s |
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| Supporting hardness | | | 72 |
| LapShearStrength | | | 9.16 MPa |
| Volume resistivity | | | 4E-04 ohms·cm |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| DegradationTemperature | | | 407 °C |
| Operating | | | -55到200 °C |
| Operating | | | -55到300 °C |
| Operating | | | 6.65 GPa |
| Operating | | | 4.80 |
| WeightLossonHeating | | | 0.48 % |
| WeightLossonHeating | | | 1.1 % |
| WeightLossonHeating | | | 1.7 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | | >80.0 °C |
| | | 4.7E-05 cm/cm/°C |
| | | 2E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | | | 3.3 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.