ABS EX58F-NA1000 SABIC INNOVATIVE MEXICO

Form：Granules | Grade：Withdrawal level

Properties:

High impact resistance

Typical Applications:

Electrical appliancesArchitectural application fieldAutomotive interior parts

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical appliances \| Architectural application field \| Automotive interior parts
Properties:	High impact resistance

Certificates

No Data...

Technical Data Sheet

Filling analysis	Test Condition	Test Method	Test Result	Test Unit
Melt viscosity	240°C, 100 sec^-1	ASTM D3835	1550	Pa·s
impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C, Total Energy	ASTM D3763	37.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5 mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	Yield, 50.0 mm Span4	ASTM D790	66.0	Mpa
bending strength	bending strength	--5,6	ISO 178	60.0	Mpa
Bending modulus	--5	ISO 178	2000	Mpa
Bending modulus	Bending modulus	50.0 mm Span4	ASTM D790	2160	Mpa
elongation	Break	ISO 527-2/50	21	%
	elongation	Break3	ASTM D638	32	%
		elongation	Yield	ISO 527-2/50	2.6	%
		elongation	elongation	Yield3	ASTM D638	3.1	%
tensile strength	Break	ISO 527-2/50	30.0	Mpa
	tensile strength	Break3	ASTM D638	30.0	Mpa
		tensile strength	Yield	ISO 527-2/50	41.0	Mpa
		tensile strength	tensile strength	Yield3	ASTM D638	39.0	Mpa
Tensile modulus	--	ISO 527-2/1	1970	Mpa
Tensile modulus	Tensile modulus	--2	ASTM D638	2080	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI Elec		UL 746	60.0	°C
RTI Imp		UL 746	60.0	°C
Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	1.0E-4	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	1.0E-4	cm/cm/°C
Vicat softening temperature	--	ISO 306/B120	97.0	°C
	Vicat softening temperature	--	ISO 306/B50	95.0	°C
	Vicat softening temperature	Vicat softening temperature	--	ASTM D15259	106	°C
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8	ISO 75-2/Af	78.0	°C
	Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	76.0	°C
	Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	91.0	°C
RTI		UL 746	60.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	220°C/10.0 kg	ISO 1133	4.0	g/10 min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.60 - 0.80	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Arc resistance		ASTM D495	PLC 5
Compared to the anti leakage trace index		UL 746	PLC 0
High arc combustion index		UL 746	PLC 4
High voltage arc tracing rate		UL 746	PLC 1
Hot wire ignition		UL 746	PLC 4
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	102

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.