Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTMD1238 | 11 g/10min |
| melt mass-flow rate | | ISO1133 | 11 g/10min |
| Shrinkage rate | | ASTMD955 | 0.40to0.48 % |
| Shrinkage rate | | ASTMD955 | 0.41to0.51 % |
| Shrinkage rate | | ISO2577 | 0.41to0.51 % |
| Shrinkage rate | | ISO2577 | 0.40to0.48 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 114 |
| Rockwell hardness | | ISO2039-2 | 114 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| | ASTMD790 | 77.0 Mpa |
| Bending stress | | ISO178 | 79.0 Mpa |
| Tensile modulus | | ASTMD638 | 2200 Mpa |
| tensile strength | | ASTMD638 | 51.0 Mpa |
| Tensile stress | | ISO527-2/5 | 53.0 Mpa |
| tensile strength | | ASTMD638 | 39.0 Mpa |
| elongation | | ASTMD638 | 30 % |
| Flexural modulus | | ASTMD790 | 2300 Mpa |
| Flexural modulus | | ISO178 | 2350 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| CharpyNotchedImpactStrength5 | | ISO179/1eA | 5.8 kJ/m² |
| Suspended wall beam gap impact strength 5 | | ISO180/1A | 6.0 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 86.0 °C |
| | ISO75-2/A | 98.0 °C |
| vicat | | ISO306/B50 | 98.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare