PC LEXAN™ HPS6R-1125
27
- Properties:High mobility
- Usages:medical caremedicine
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTMD1238 | 7.0 g/10min | |
| ASTMD1238 | 110 g/10min | ||
| Melt volume flow rate | ISO1133 | 6.50 cm3/10min | |
| Shrinkage rate | 内部方法 | 0.50to0.70 % | |
| 内部方法 | 0.50to0.70 % | ||
| 内部方法 | 0.50to0.70 % | ||
| Water absorption rate | ASTMD570 | 0.15 % | |
| ISO62 | 0.35 % | ||
| ISO62 | 0.15 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTMD785 | 118 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus 3 | ASTMD638 | 2310 Mpa | |
| Tensile modulus | ISO527-2/1 | 2300 Mpa | |
| Tensile strength 4 | ASTMD638 | 62.1 Mpa | |
| Tensile stress | ISO527-2/50 | 60.0 Mpa | |
| Tensile strength 4 | ASTMD638 | 68.9 Mpa | |
| Tensile stress | ISO527-2/50 | 75.0 Mpa | |
| elongation | ASTMD638 | 6.5 % | |
| Tensile strain | ISO527-2/50 | 6.0 % | |
| elongation | ASTMD638 | 140 % | |
| Tensile strain | ISO527-2/50 | 140 % | |
| Flexural modulus | ASTMD790 | 2340 Mpa | |
| Bending modulus 6 | ISO178 | 2250 Mpa | |
| Bending strength 6,7 | ISO178 | 95.0 Mpa | |
| Flexural Strength5 | ASTMD790 | 97.9 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam gap 8 | ISO179/1eA | 15 kJ/m² | |
| ISO179/1eA | 75 kJ/m² | ||
| Simple supported beam without notch impact strength 8 | ISO179/1eU | NoBreak | |
| ISO179/1eU | NoBreak | ||
| Suspended wall beam gap impact strength 9 | ISO180/1A | 10 kJ/m² | |
| ISO180/1A | 70 kJ/m² | ||
| Unscented Izod Impact Strength 9 | ISO180/1U | NoBreak | |
| ISO180/1U | NoBreak | ||
| Dart impact equipped with measuring instruments | ASTMD3763 | 65.0 J | |
| ASTMD3763 | 65.0 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ASTME831 | 5.7E-05 cm/cm/°C | ||
| ISO11359-2 | 6E-05 cm/cm/°C | ||
| Heat distortion temperature | ASTMD648 | 138 °C | |
| ASTMD648 | 124 °C | ||
| ASTMD648 | 132 °C | ||
| Hot deformation temperature 10 | ISO75-2/Af | 124 °C | |
| vicat | ASTMD152511 | 154 °C | |
| ISO306/B50 | 143 °C | ||
| ISO306/B120 | 140 °C | ||
| BallPressure Test | IEC60695-10-2 | Pass | |
| ASTME831 | 6.2E-05 cm/cm/°C | ||
| ISO11359-2 | 6E-05 cm/cm/°C | ||
| Heat distortion temperature | ASTMD648 | 135 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.