Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.70 g/cm³ |
| Shrinkage rate | | ISO2577 | 0.15 % |
| Shrinkage rate | | DIN53464 | 0.0 % |
| Water absorption rate | | ISO62 | <0.50 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Hot filament ignition temperature | | IEC60695-2-13 | 960 °C |
| Limiting Oxygen Index | | ISO4589-2 | 32 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| GlowBar | | IEC60707-3 | LevelBH2<=10 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | Compression Molded | ISO527-2 | 11000 MPa |
| Tensile stress | | ISO527-2 | 66.0 MPa |
| Flexural modulus | Compression Molded | ISO178 | 10000 MPa |
| Bending stress | Compression Molded | ISO178 | 158 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | Compression Molded | ISO179 | 71 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| CTI | | IEC60112 | 600 V |
| Surface Resistivity | | IEC60093 | 1E+12 ohms |
| Volume resistivity | | IEC60093 | 1E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | >200 °C |
| Continuous use temperature | | 内部方法 | 165 °C |
| Glass Transition Temperature | | DSC | 170 °C |
| | ISO11359-2 | 1.2E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.